Albumin suppresses oxidation of TiNb alloy in the simulated inflammatory environment.

Literature data has shown that reactive oxygen species (ROS), generated by immune cells during post-operative inflammation, could induce corrosion of standard Ti-based biomaterials. For Ti6Al4V alloy, this process can be further accelerated by the presence of albumin. However, this phenomenon remains unexplored for Ti ß-phase materials, such as TiNb alloys. These alloys are attractive due to their relatively low elastic modulus value. This study aims to address the question of how albumin influences the corrosion resistance of TiNb alloy under simulated inflammation. Electrochemical and ion release tests have revealed that albumin significantly enhances corrosion resistance over both short (2 and 24 h) and long (2 weeks) exposure periods. Furthermore, post-immersion XPS and cross-section TEM analysis have demonstrated that prolonged exposure to an albumin-rich inflammatory solution results in the complete coverage of the TiNb surface by a protein layer. Moreover, TEM studies revealed that H2O2-induced oxidation and further formation of a defective oxide film were suppressed in the solution enriched with albumin. Overall results indicate that contrary to Ti6Al4V, the addition of albumin to the PBS + H2O2 solution is not necessary to simulate the harsh inflammatory conditions as could possibly be found in the vicinity of a TiNb implant.

Thermal Stability and Mechanical Behavior of Ultrafine-Grained Titanium with Different Impurity Content.

Ultrafine-grained (UFG) commercially pure (Ti Grade 2) and high-purity (Ti 99.99%) titanium can be a good alternative to less biocompatible Ti alloys in many biomedical applications. Their severe plastic deformation may lead to a substantial increase of strength, but their highly refined microstructure show a lower thermal stability which may limit their range of applications. The purpose of this study was to investigate the effect of interstitial elements on the thermal stability of UFG Ti Grade 2 and high-purity Ti 99.99% processed by a multi-pass cold rolling to the total thickness reduction of 90%. The severely cold rolled Ti sheets were annealed at temperature in the range of 100-600 °C for 1 h and, subsequently, they were evaluated in terms of microstructure stability, mechanical performance as well as heat effects measured by differential scanning calorimetry (DSC). It was found that the microstructure and mechanical properties were relatively stable up to 200 and 400 °C in the case of UFG Ti 99.99% and Ti Grade 2, respectively. DSC measurements confirmed the aforementioned results about lower temperature of recovery and recrystallization processes in the high-purity titanium. Surprisingly, the discontinuous yielding phenomenon occurred in both investigated materials after annealing above their thermal stability range, which was further discussed based on their microstructural characteristics. Additionally, the so-called hardening by annealing effect was observed within their thermal stability range (i.e., at 100-400 °C for UFG Ti Grade 2 and 100 °C for UFG Ti 99.99%).

How Streptococcus mutans Affects the Surface Topography and Electrochemical Behavior of Nanostructured Bulk Ti.

The metabolization of carbohydrates by Streptococcus mutans leads to the formation of lactic acid in the oral cavity, which can consequently accelerate the degradation of dental implants fabricated from commercially available microcrystalline Ti. Microstructure influences surface topography and hence interaction between bacteria cells and Ti surfaces. This work offers the first description of the effect of S. mutans on the surface topography and properties of nanostructured bulk Ti, which is a promising candidate for modern narrow dental implants owing to its superior mechanical strength. It was found that S. mutans incubation resulted in the slight, unexpected decrease of surface nanoroughness, which was previously developed owing to privileged oxidation in areas of closely spaced boundaries. However, despite the changes in nanoscale surface topography, bacteria incubation did not reduce the high level of protection afforded by the oxide layer formed on the nanostructured Ti surface. The results highlight the need-hitherto ignored-to consider Ti microstructure when analyzing its behavior in the presence of carbohydrate-metabolizing bacteria.

Corrosion Behavior of Cold-Formed AA5754 Alloy Sheets.

In this work, the influence of bending an AA5457 alloy sheet and the resulting microstructural changes on its corrosion behavior was investigated. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to perform detailed microstructural analyses of the alloy in its original form and after bending. After immersion in naturally-aged NaCl under open-circuit conditions (0.5 M, adjusted to 3 by HCl), post-corrosion observations were made, and electrochemical polarization measurements were performed to investigate the corrosion mechanisms occurring on both surfaces. The results showed that the corrosion of AA5457 is a complex process that mainly involves trenching around coarse Si-rich particles, crystallographically-grown large pits, and the formation of multiple tiny pits around Si-rich nanoparticles. The experimental data showed that bending AA5457 changed the shape and distribution of Si-rich coarse particles, cumulated a higher dislocation density in the material, especially around Si-rich nanoparticles, and all of these factors caused that corrosion behavior of the AA5754 in the bending area was lowered.

Hydrostatic Extrusion and Nano-Hardness of Nanocrystalline Grade 2 Titanium.

The structure and corrosion resistance of Grade 2 titanium subjected to the hydroextrusion processes were examined. The microstructure was characterized using optical microscopy and transmission electron microscopy. The corrosion resistance was determined using the impedance and potentiodynamic methods, in 0.1 M H2SO4 solutions and an acidified 0.1 M NaCl solution with a pH of 4.2, at ambient temperature. Nanohardness tests were performed under a load of 100 mN. It has been demonstrated that the hydroextrusion method makes it possible to obtain relatively homogeneous nanocrystalline titanium Grade 2 with an increased hardness, the elastic modulus almost unchanged with respect to that of the initial structure and a lower corrosion resistance.

Comparative laser spectroscopy diagnostics for ancient metallic artefacts exposed to environmental pollution.

Metal artworks are subjected to corrosion and oxidation processes due to reactive agents present in the air, water and in the ground that these objects have been in contact with for hundreds of years. This is the case for archaeological metals that are recovered from excavation sites, as well as artefacts exposed to polluted air. Stabilization of the conservation state of these objects needs precise diagnostics of the accrued surface layers and identification of original, historical materials before further protective treatments, including safe laser cleaning of unwanted layers. This paper presents analyses of the chemical composition and stratigraphy of corrosion products with the use of laser induced breakdown spectroscopy (LIBS) and Raman spectroscopy. The discussion of the results is supported by material studies (SEM-EDS, XRF, ion-analyses). The tests were performed on several samples taken from original objects, including copper roofing from Wilanów Palace in Warsaw and Karol Poznanski Palace in LódY, bronze decorative figures from the Wilanów Palace gardens, and four archaeological examples of old jewellery (different copper alloys). Work has been performed as a part of the MATLAS project in the frames of EEA and Norway Grants (www.matlas.eu) and the results enable the comparison of the methodology and to elaborate the joint diagnostic procedures of the three project partner independent laboratories.

Structural and mechanical properties of nanocrystalline titanium and 316LVM steel processed by hydrostatic extrusion.

The aim of the present study was to examine the potential of hydrostatic extrusion for the fabrication of high-strength materials for medical applications. The materials examined were 316LVM steel and technically pure titanium. The microstructures and mechanical properties of the materials before and after hydrostatic extrusion were analysed. It was found that the hydrostatic extrusion process resulted in a substantial refinement of the material microstructures. The refinement of the microstructure was accompanied by an improvement of the mechanical properties, such as the microhardness and yield stress.